Description：
Stable
welding can be performed with good us-ability and
welding ability . Due to more Mo content than that of
C-316, its corrosion resistibility is superior in dilute
sulphric acid. As weld metal with ultra-low carbon
content can be obtained, it shows good inter granular
corrosion resistibility.
Application：
For welding of
19%Cr-13%Ni-Mo (SUS 317) stainless steel.
Typical weld
metal properties： (Weld Metal Analysis)
Carbon
………………………………………………………… 0.025
Manganese ……………………………………………………. 1.29
Silicon ………………………………………………………… 0.57
Phosphorus ……………………………………………………. 0.014
Sulphur ……………………………………………………….. 0.011
Chromium…………………………………………………….. 19.50
Molybdenun……………………………………………………3.50
Nickel ……………………………………………………….. 13.95
Niobium ……………………………………………………. ------
Mechanical
properties:
Tensile Strength (Kg/mm2)
………………………………... 53.0 ~ 60.0
Yield Point (Kg/mm2) ……………………………………... ----
Elongation (%) …………………………………………….. 30.0 ~ 42.0
Reduction of Area (%) …………………………………….. ----
Available diameter and recommended operating ranges：
| |
F.
& H. – fillet |
V.
& O.H. |
2.6 X300 m/m
3.2 X350 m/m
4.0 X350 m/m
5.0 X350 m/m |
50 ~
85 Amps
85 ~ 110 Amps
110 ~ 140 Amps
140 ~ 190 Amps |
45 ~ 80 Amps
70 ~ 90 Amps
90~130 Amps |
Type
of power：A.C. or D.C.E.P.
Approvals：
⃞ |